In special printing, glass substrates
There are several suitable for decorative glass printing ink.Porcelain ink contains ground into a fine powder or glass material and inorganic pigments and at more than 600 ℃ temperature roasting.Porcelain ink contain oily medium, it add the inorganic pigments, glass material and filling agent spread out and can be printed by steel, polyester, nylon nets, in pigment and firing into the glass, glass ware before to agents, the operating process must be (1 -) 1.5 h.During this period, the glass before cooling temperature rise to (600-650) ℃ to 10 min, the disadvantage of this method is for multi-color printing is not suitable, previously printed color will be shed by the back of the screen printing color.That is designed on the glass printing and the same is true for a two-component epoxy resin ink.But in the case of monochrome printing ceramic ink for the drink cosmetics company, the reason is that screen printing image and visual impact of ink thickness.
Screen printing ceramic ink and glass enamels in annealing furnace fire, sturdy and can produce high-quality images, however, in the process for decoration beverage drink cosmetics glass container is slow and expensive.Annealing furnace can use a lot of, the temperature change will cause the color change.Ink system also is limited by the design, because the resolution of the printing image by ceramic, enamel required minimum restrictions on the size of mesh.Thermoplastic (TP) ink, also called hot melt ink, for the solid state at room temperature, need to be heated to a printable, ink preheating (65-75) ℃, combine porcelain glaze melt through the current heating wire mesh.Molten oil mozi ah it act like a normal ink through the screen, but when it encounters cool glass, it becomes solid and restore to the soft state.TP ink satisfactorily suitable for automatic, multicolor printing, however.Once printing multicolor image slightly brittle, it needs to be organic pigment and the resin in the annealing furnace temperature calcination at 200 ℃.
By roasting ink the biggest advantage is that they bearing and seal material melt and become a part of it, such as gold, silver, palladium and platinum metals also can be used as a pigment bearing and seal on the glass and ceramics for decorative or industrial applications, the main drawback is the use of the complexity and cost of the annealing furnace.UV printing ink method as well as on the plastic and cardboard printing.Organic pigment and the resin drying UV radiation.Can be far less than the annealing furnace, used in the UV drying and ink dry immediately.Adhesion force on the glass of preheating is wonderful, for the treatment of the glass is good, UV not as strong as of roasting porcelain glaze, but it is still a lot of application can accept a substitute,
Printing complex, is the most effective method of multicolor image printed on transfer paper, and the way to stick with water decal paper printed graphics, image quality is unique, you can use many colors.Four-color printing need white color, the base can be printed.
Car decoration is very significant in the glass printing.Printing the anti-glare film and filter membrane in automobile windshield plane, like circuit (defroster) and antenna.Architectural glass is another area in general use printing, screen printing effect can give building appreciation, even with a picture of the exotic indoor partition will work environment.
OLAT printing machine series ceramic can be in ceramics, glass, automotive interior accurate printing, can be realized on the object surface, a plane is the most beautiful and high quality printing effect.In terms of color selection, nicky oulette launched monochrome, two-color, three color, four color, six color machine, can choose according to need to machine.